1. WO2020000592 - TUNNEL KILN STACK FIRING METHOD FOR FOAMED CERAMIC LIGHTWEIGHT BOARD

Publication Number WO/2020/000592
Publication Date 02.01.2020
International Application No. PCT/CN2018/100135
International Filing Date 11.08.2018
IPC
C CHEMISTRY; METALLURGY
04
CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
B
LIME; MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
33
Clay-wares
02
Preparing or treating the raw materials individually or as batches
13
Compounding ingredients
132
Waste materials; Refuse
C CHEMISTRY; METALLURGY
04
CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
B
LIME; MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
33
Clay-wares
02
Preparing or treating the raw materials individually or as batches
13
Compounding ingredients
C CHEMISTRY; METALLURGY
04
CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
B
LIME; MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
33
Clay-wares
32
Burning methods
C CHEMISTRY; METALLURGY
04
CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
B
LIME; MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
38
Porous mortars, concrete, artificial stone or ceramic ware; Preparation thereof
02
by adding chemical blowing agents
C04B 33/132 (2006.01)
C04B 33/13 (2006.01)
C04B 33/32 (2006.01)
C04B 38/02 (2006.01)
CPC
C04B 2235/3463
C04B 2235/349
C04B 2235/77
C04B 2235/96
C04B 2235/9607
C04B 33/131
Applicants
  • 广东科达洁能股份有限公司 KEDA CLEAN ENERGY CO., LTD. [CN/CN]; 中国广东省佛山市 顺德区陈村镇广隆工业园环镇西路1号 No.1, Huanzhen Xi Road, Guanglong Industrial Zone, Chencun, Shunde Foshan, Guangdong 528313, CN
Inventors
  • 林智 LIN, Zhi; CN
Agents
  • 广州圣理华知识产权代理有限公司 GUANGZHOU SHENGLIHUA-IP AGENT LTD; 中国广东省广州市 天河区体育西路103号维多利广场A座46楼 Floor 46, Building A, Victory Plaza, No.103, Tiyu West Road, Tianhe District Guangzhou, Guangdong 510620, CN
Priority Data
201810687030.228.06.2018CN
Publication Language Chinese (ZH)
Filing Language Chinese (ZH)
Designated States
Title
(EN) TUNNEL KILN STACK FIRING METHOD FOR FOAMED CERAMIC LIGHTWEIGHT BOARD
(FR) PROCÉDÉ DE CUISSON EN EMPILEMENT EN FOUR TUNNEL POUR PANNEAU LÉGER EN CÉRAMIQUE EXPANSÉE
(ZH) 一种发泡陶瓷轻质板材的隧道窑叠烧方法
Abstract
(EN)
A tunnel kiln stacking firing method for a foamed ceramic lightweight board, comprising: (1) mixing raw materials according to a proportion, ball milling, and spray drying to obtain a powder material, wherein the raw materials comprise tile polishing waste residue, clay, feldspar, a foaming agent and a stabilizer, the stabilizer being manganese dioxide; (2) distributing the powder material on a kiln cart, wherein the kiln cart comprises a support, and the support is provided thereon with at least three layers of saggars, the saggars being used for distributing and molding the powder material; (3) pushing the kiln cart into a tunnel kiln for multi-layer stacking firing treatment, wherein the firing temperature is 1150-1220°C, and the firing cycle is 15-24 hours. The method achieves low-temperature fast firing, and foamed ceramic lightweight boards obtained by the firing therein are located on the same cross section, no difference existing between between pores from top to bottom, and uniformity being high.
(FR)
La présente invention concerne un procédé de cuisson par empilement en four tunnel pour un panneau léger en céramique expansée, comprenant : (1) le mélange de matières premières selon une proportion, le broyage à boulets et le séchage par pulvérisation pour obtenir un matériau en poudre, les matières premières comprenant des résidus de déchets de polissage de tuile, de l'argile, du feldspath, un agent moussant et un stabilisant, le stabilisant étant du dioxyde de manganèse; (2) la distribution du matériau en poudre sur un chariot de four, le chariot de four comprenant un support, et le support ayant sur lui au moins trois couches de casettes, les casettes étant utilisées pour distribuer et mouler le matériau en poudre; (3) la poussée du chariot de four dans un four tunnel pour un traitement de cuisson en empilement multicouche, la température de cuisson étant comprise entre 1 150 et 1 220 °C, et le cycle de cuisson étant compris entre 15 et 24 heures. Le procédé permet une cuisson rapide à basse température, et les panneaux légers en céramique expansée obtenus par cuisson de l'intérieur de ces derniers sont situés sur la même section transversale, aucune différence n'existant entre les pores de haut en bas et l'uniformité étant élevée.
(ZH)
一种发泡陶瓷轻质板材的隧道窑叠烧方法,包括:(1)将原料按配比混料,并经球磨、喷雾干燥,得到粉料,其中,原料包括瓷砖抛光废渣、粘土、长石、发泡剂和稳定剂,稳定剂为二氧化锰;(2)将粉料在窑车上进行布料,其中,窑车包括支架,支架上设有至少三层匣钵,匣钵用于粉料的布料成型;(3)将窑车推入隧道窑进行多层叠烧处理,烧成温度为1150-1220℃,烧成周期为15-24小时。该方法实现低温快烧,其烧成得到的发泡陶瓷轻质板材在同一断面上,从上到下气孔无差异,气泡均匀性高。