1. WO2019051747 - METHOD FOR PREPARING COMPOSITE FILM OF MULTILAYER CARBOXYMETHYL CHITOSAN

Publication Number WO/2019/051747
Publication Date 21.03.2019
International Application No. PCT/CN2017/101812
International Filing Date 15.09.2017
IPC
B01D 69/00 2006.01
BPERFORMING OPERATIONS; TRANSPORTING
01PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
DSEPARATION
69Semi-permeable membranes for separation processes or apparatus characterised by their form, structure or properties; Manufacturing processes specially adapted therefor
B01D 69/12 2006.01
BPERFORMING OPERATIONS; TRANSPORTING
01PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
DSEPARATION
69Semi-permeable membranes for separation processes or apparatus characterised by their form, structure or properties; Manufacturing processes specially adapted therefor
12Composite membranes; Ultra-thin membranes
CPC
B01D 69/00
BPERFORMING OPERATIONS; TRANSPORTING
01PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
DSEPARATION
69Semi-permeable membranes for separation processes or apparatus characterised by their form, structure or properties; Manufacturing processes specially adapted therefor
B01D 69/12
BPERFORMING OPERATIONS; TRANSPORTING
01PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
DSEPARATION
69Semi-permeable membranes for separation processes or apparatus characterised by their form, structure or properties; Manufacturing processes specially adapted therefor
12Composite membranes; Ultra-thin membranes
Applicants
  • 熊德峰 XIONG, Defeng [CN]/[CN]
Inventors
  • 熊德峰 XIONG, Defeng
Priority Data
201710825570.814.09.2017CN
Publication Language Chinese (ZH)
Filing Language Chinese (ZH)
Designated States
Title
(EN) METHOD FOR PREPARING COMPOSITE FILM OF MULTILAYER CARBOXYMETHYL CHITOSAN
(FR) PROCÉDÉ DE PRÉPARATION D'UN FILM COMPOSITE DE CARBOXYMÉTHYLCHITOSANE MULTICOUCHE
(ZH) 一种多层羧甲基壳聚糖复合膜的制备方法
Abstract
(EN)
Disclosed is a method for preparing a composite film of multilayer carboxymethyl chitosan, comprising the following steps: placing 3-7 parts of CMCS into 30-40 parts of distilled water, stirring same on a magnetic stirrer until completely dissolved, and filtering and degassing same, immersing a base film in distilled water for 20-24 h, taking same out, air drying and sticking same to a dried glass plate, uniformly coating the base film with the above solution, standing same for 1-3 h and taking same out for filtering and drying, drying at 50-55ºC, then crosslinking same with a 2% glutaraldehyde solution for 15-25 min, and repeatedly washing same clean with distilled water and drying at room temperature, and repeating the above steps several times, so as to obtain the multilayer CMCS composite film, with each raw material being in parts by weight. The method has a simple process, and the composite film prepared has a large flux, is economical and environmentally friendly, and can be produced on a large scale.
(FR)
L'invention concerne un procédé de préparation d'un film composite de carboxyméthylchitosane multicouche, comprenant les étapes suivantes : placer de 3 à 7 parties de CMCS dans 30 à 40 parties d'eau distillée, agiter à l'aide d'un agitateur magnétique jusqu'à une dissolution complète, en effectuer le filtrage et le dégazage, immerger un film de base dans de l'eau distillée de 20 à 24 h, le retirer, le faire sécher à l'air et le coller à une plaque de verre sec, enduire uniformément le film de base avec la solution ci-dessus, laisser reposer de 1 à 3 h, le retirer pour le filtrer et le sécher entre 50 et 55 °C, puis effectuer une réticulation avec une solution de glutaraldéhyde à 2 % pendant 15 à 25 min, le laver de manière répétée avec de l'eau distillée, le sécher à température ambiante, et répéter les étapes ci-dessus plusieurs fois de façon à obtenir le film composite CMCS multicouche, chaque matière première étant en parties en poids. Le procédé est simple, et le film composite préparé présente un fondant important, est économique et respectueux de l'environnement, et peut être produit à grande échelle.
(ZH)
一种多层羧甲基壳聚糖复合膜的制备方法,步骤如下:将3-7份CMCS放入30-40份蒸馏水中,在磁力搅拌器上搅拌至完全溶解,过滤,脱气;将基膜放入蒸馏水中浸泡20-24h,取出晾干,粘在干燥的玻璃板上,将上述溶液均匀地涂覆在基膜上,静置1-3h,取出滤干,50-55℃下干燥后,用2%的戊二醛溶液交联15-25min,再用蒸馏水反复洗涤干净,在室温下干燥,多次重复上述步骤即得多层CMCS复合膜;各原料均为重量份。该方法工艺简单,制得的复合膜通量较大,经济环保,可大规模生产。