1. WO2016021193 - HIGH-STRENGTH STEEL SHEET AND PRODUCTION METHOD FOR SAME, AND PRODUCTION METHOD FOR HIGH-STRENGTH GALVANIZED STEEL SHEET

Publication Number WO/2016/021193
Publication Date 11.02.2016
International Application No. PCT/JP2015/003943
International Filing Date 05.08.2015
IPC
C22C 38/00 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
C21D 9/46 2006.01
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING, OR OTHER TREATMENTS
9Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
46for sheet metals
C22C 38/04 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
04containing manganese
C22C 38/60 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
60containing lead, selenium, tellurium or antimony, or more than 0.04% by weight of sulfur
C22C 18/04 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
18Alloys based on zinc
04with aluminium as the next major constituent
CPC
C21D 2211/001
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
2211Microstructure comprising significant phases
001Austenite
C21D 2211/002
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
2211Microstructure comprising significant phases
002Bainite
C21D 2211/005
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
2211Microstructure comprising significant phases
005Ferrite
C21D 2211/008
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
2211Microstructure comprising significant phases
008Martensite
C21D 6/005
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
6Heat treatment of ferrous alloys
005containing Mn
C21D 6/008
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
6Heat treatment of ferrous alloys
008containing Si
Applicants
  • JFEスチール株式会社 JFE STEEL CORPORATION [JP]/[JP]
Inventors
  • 川崎 由康 KAWASAKI, Yoshiyasu
  • 松田 広志 MATSUDA, Hiroshi
  • 小幡 美絵 OBATA, Yoshie
  • 金子 真次郎 KANEKO, Shinjiro
  • 横田 毅 YOKOTA, Takeshi
  • 瀬戸 一洋 SETO, Kazuhiro
Agents
  • 杉村 憲司 SUGIMURA, Kenji
Priority Data
2014-16167207.08.2014JP
Publication Language Japanese (JA)
Filing Language Japanese (JA)
Designated States
Title
(EN) HIGH-STRENGTH STEEL SHEET AND PRODUCTION METHOD FOR SAME, AND PRODUCTION METHOD FOR HIGH-STRENGTH GALVANIZED STEEL SHEET
(FR) TÔLE D'ACIER À HAUTE RÉSISTANCE AINSI QUE PROCÉDÉ DE FABRICATION DE CELLE-CI, ET PROCÉDÉ DE FABRICATION DE TÔLE D'ACIER GALVANISÉ À HAUTE RÉSISTANCE
(JA) 高強度鋼板およびその製造方法、ならびに高強度亜鉛めっき鋼板の製造方法
Abstract
(EN)
 The present invention provides a high-strength steel sheet having a tensile strength (TS) of at least 780 MPa, excellent ductility and stretch flangeability, and excellent material-quality stability, achieved by: having a specific component composition; the steel structure having, in terms of area ratio, a total of ferrite and bainitic ferrite of 25-80%, and 3-20% martensite, and having, in terms of volume fraction, at least 10% retained austenite; the average crystalline particle diameter of the retained austenite being not more than 2μm; the average Mn volume (mass%) in the retained austenite being at least 1.2 times the Mn volume (mass%) in the steel; and the area ratio of retained austenite that has an average C volume (mass%) of at least 2.1 times the C volume (mass%) of the steel being at least 60% of the area ratio of the total retained austenite.
(FR)
Selon l'invention, il est possible d'obtenir une tôle d'acier à haute résistance excellente non seulement en termes de ductilité mais aussi d'aptitude au formage des bords par étirage, et également dotée d'une excellente stabilité des matériaux. Cette tôle d'acier à haute résistance possède une composition prédéfinie. La composition d'acier de l'objet de l'invention, est telle que : en rapport surfacique, la somme d'une ferrite et d'une ferrite bainitique est supérieure ou égale à 25% et inférieure ou égale à 80% et une martensite est supérieure ou égale à 3% et inférieure ou égale à 20% ; en rapport volumique, une austénite résiduelle est supérieure ou égale à 10% ; le diamètre de grain cristallin moyen de l'austénite résiduelle est inférieur ou égal à 2µm ; et la quantité moyenne de Mn (en % en masse) contenu dans l'austénite résiduelle est supérieure ou égale à 1,2 fois la quantité de Mn (en % en masse) contenu dans l'acier. Enfin, le rapport surfacique de l'austénite résiduelle qui possède une quantité moyenne de C (en % en masse) supérieure ou égale à 2,1 fois la quantité de C (en % en masse) contenu dans l'acier, est supérieur ou égal à 60% du rapport surfacique de l'ensemble de l'austénite résiduelle, ainsi, la tôle d'acier à haute résistance possède une résistance à la traction (TS) supérieure ou égale à 780MP en rapport surfacique.
(JA)
 本発明に従い、所定の成分組成を有し、鋼組織を、面積率で、フェライトとベイニティックフェライトの合計:25%以上80%以下、マルテンサイト:3%以上20%以下とし、体積率で、残留オーステナイト:10%以上とし、さらに、残留オーステナイトの平均結晶粒径を2μm以下として、残留オーステナイト中の平均Mn量(質量%)を鋼中のMn量(質量%)の1.2倍以上とし、加えて、鋼中のC量(質量%)の2.1倍以上の平均C量(質量%)を有する残留オーステナイトの面積率を、全残留オーステナイトの面積率の60%以上とすることによって、780MPa以上の引張強度(TS)を有し、延性のみならず伸びフランジ性にも優れ、さらには材質安定性にも優れる高強度鋼板を得ることができる。