1. WO2014154106 - LOW-ALLOY HIGH-HARDNESS WEAR-RESISTANT STEEL PLATE AND MANUFACTURING METHOD THEREFOR

Publication Number WO/2014/154106
Publication Date 02.10.2014
International Application No. PCT/CN2014/073680
International Filing Date 19.03.2014
IPC
C22C 38/14 2006.01
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
38Ferrous alloys, e.g. steel alloys
14containing titanium or zirconium
C21D 8/02 2006.01
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING, OR OTHER TREATMENTS
8Modifying the physical properties by deformation combined with, or followed by, heat treatment
02during manufacturing of plates or strips
CPC
C21D 1/25
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
1General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
18Hardening
25Hardening, combined with annealing between 300 degrees Celsius and 600 degrees Celsius, i.e. heat refining ("Vergüten")
C21D 2211/001
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
2211Microstructure comprising significant phases
001Austenite
C21D 2211/008
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
2211Microstructure comprising significant phases
008Martensite
C21D 6/001
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
6Heat treatment of ferrous alloys
001containing Ni
C21D 6/002
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
6Heat treatment of ferrous alloys
002containing Cr
C21D 6/004
CCHEMISTRY; METALLURGY
21METALLURGY OF IRON
DMODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
6Heat treatment of ferrous alloys
004containing Cr and Ni
Applicants
  • 宝山钢铁股份有限公司 BAOSHAN IRON & STEEL CO., LTD. [CN]/[CN]
Inventors
  • 李红斌 LI, Hongbin
  • 姚连登 YAO, Liandeng
  • 宋国斌 SONG, Guobin
Agents
  • 上海专利商标事务所有限公司 SHANGHAI PATENT & TRADEMARK LAW OFFICE, LLC
Priority Data
201310105177.328.03.2013CN
Publication Language Chinese (ZH)
Filing Language Chinese (ZH)
Designated States
Title
(EN) LOW-ALLOY HIGH-HARDNESS WEAR-RESISTANT STEEL PLATE AND MANUFACTURING METHOD THEREFOR
(FR) TÔLE D'ACIER RÉSISTANT À L'USURE, À DURETÉ ÉLEVÉE ET FAIBLEMENT ALLIÉ, ET PROCÉDÉ DE FABRICATION DE CETTE DERNIÈRE
(ZH) 一种低合金高硬度耐磨钢板及其制造方法
Abstract
(EN)
a low-alloy high-hardness wear-resistant steel plate having the following chemical composition (wt %): C: 0.33-0.45%; Si: 0.10-0.50%; Mn: 0.50-1.50%; B: 0.0005-0.0040%; Cr≤1.50%; Mo≤0.80%; Ni≤2.00%; Nb≤0.080%; V≤0.080%; Ti≤0.060%; RE≤0.10%; W≤1.00%; Al: 0.010%-0.080%; Ca: 0.0010-0.0080%; N≤0.0080%; O≤0.0080%; H≤0.0004%; P≤0.015%; and S≤0.010%, such that 0.20%≤(Cr/5+Mn/6+50B)≤0.50%; 0.02%≤(Mo/3+Ni/5+2Nb)≤0.50%; 0.01%≤(Al+Ti)≤0.13%, and the balance is Fe and unavoidable purities. The above chemical composition and thermal processing are used to obtain a steel plate that has a high degree of hardness and outstanding wear resistance and that is thereby suitable for use in all manner of machine parts susceptible to wear and tear.
(FR)
La présente invention se rapporte à une tôle d'acier résistant à l'usure, à dureté élevée et faiblement allié, qui présente la composition chimique suivante (% en poids) : une quantité de carbone (C) comprise entre 0,33 et 0,45 % ; une quantité de silicium (Si) comprise entre 0,10 et 0,50 % ; une quantité de manganèse (Mn) comprise entre 0,50 et 1,50 % ; une quantité de bore (B) comprise entre 0,0005 et 0,0040 % ; une quantité de chrome (Cr) inférieure ou égale à 1,50 % ; une quantité de molybdène (Mo) inférieure ou égale à 0,80 % ; une quantité de nickel (Ni) inférieure ou égale à 2,0 % ; une quantité de niobium (Nb) inférieure ou égale à 0,080 % ; une quantité de vanadium (V) inférieure ou égale à 0,080 % ; une quantité de titane (Ti) inférieure ou égale à 0,060 % ; une quantité de rhénium (Re) inférieure ou égale à 0,10 % ; une quantité de tungstène (W) inférieure ou égale à 1,00 % ; une quantité d'aluminium (Al) comprise entre 0,10 et 0,080 % ; une quantité de calcium (Ca) comprise entre 0,0010 et 0,0080 % ; une quantité d'azote (N) inférieure ou égale à 0,0080 % ; une quantité d'oxygène (O) inférieure ou égale à 0,0080 % ; une quantité d'hydrogène (H) inférieure ou égale à 0,0004 % ; une quantité de phosphore (P) inférieure ou égale à 0,015 % ; et une quantité de soufre (S) inférieure ou égale à 0,010 % de telle sorte que 0,20 % ≤ (Cr/5 + Mn/6 + 50B) ≤ 0,50 % ; 0,02 % ≤ (Mo/3 + Ni/5 + 2Nb) ≤ 0,50 % ; 0,01 % ≤ (Al + Ti) ≤ 0,13 %, le reste étant du fer (Fe) et des impuretés inévitables. La composition chimique mentionnée ci-dessus et le traitement thermique sont utilisés pour obtenir une tôle d'acier qui présente un degré élevé de dureté et une résistance à l'usure exceptionnelle et qui est, de ce fait, appropriée pour être utilisée de cette manière dans toutes les pièces de machine sensibles à l'usure et à la détérioration.
(ZH)
一种低合金高硬度耐磨钢板,其化学成分(wt%)为C:0.33-0.45%,Si:0.10-0.50%,Mn:0.50-1.50%,B:0.0005-0.0040%,Cr≤1.50%,Mo≤0.80%,Ni≤2.00%,Nb≤0.080%,V≤0.080%,Ti≤0.060%,RE≤0.10%,W≤1.00%,Al:0.010%-0.080%,Ca:0.0010-0.0080%,N≤0.0080%,O≤0.0080%,H≤0.0004%,P≤0.015%,S≤0.010%,且满足0.20%≤(Cr/5+Mn/6+50B)≤0.50%,0.02%≤(Mo/3+Ni/5+2Nb)≤0.50%,0.01%≤(Al+Ti)≤0.13%,其余为Fe和不可避免的杂质。通过以上成分及各热处理工艺得到的钢板硬度高,耐磨性能优异,适于各种机械设备中极易磨损部件。