1. KR1020010024707 - NITRATE/NITRITE-FREE MANUFACTURING OF GLASS WITH SELENIUM

Office
Republic of Korea
Application Number 1020007006267
Application Date 09.06.2000
Publication Number 1020010024707
Publication Date 26.03.2001
Publication Kind A
IPC
C03C 1/00
CCHEMISTRY; METALLURGY
03GLASS; MINERAL OR SLAG WOOL
CCHEMICAL COMPOSITION OF GLASSES, GLAZES, OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
1Ingredients generally applicable to manufacture of glasses, glazes or vitreous enamels
Applicants FORD MOTOR COMPANY
티. 제이. 드쥐르포드 모터 캄파니
Inventors JONES JAMES VICTOR
존스,제임스,빅터
BOULOS EDWARD NASHED
불러스,에드워드,내쉬드
Agents 주성민
김영
Priority Data 08988481 10.12.1997 US
Title
(EN) NITRATE/NITRITE-FREE MANUFACTURING OF GLASS WITH SELENIUM
(KO) 질산염/아질산염을 사용하지 않고 셀레늄 함유 유리를제조하는 방법
Abstract
(EN)

The invention is a method of retaining selenium in a glass containing selenium by including a manganese compound but excluding nitrates or nitrites routinely used in the industry to retain selenium. Particularly, a preferred embodiment involves manufacturing a grey soda-lime-silica glass composition including selenium as a colorant, the components of the grey soda-lime- silica glass have colorants consisting essentially of: greater than 0.9 to 1.9 wt.% total iron oxide as Fe2 O3; 0.10 to 1.00 wt.% manganese compound as MnO2; 0.0010 to 0. 0060 wt.% selenium as Se; 0.002 to 0.025 wt.% cobalt oxide as Co, and 0 to 1.0 wt.% titanium oxide as TiO2which are combined and melted to make the glass composition. The glass composition has at 4.0 mm. thickness: 10 to 55 % light transmittance using Illuminant A, less than 25 % ultra violet transmittance, and less than 50 % infrared transmittance.

© KIPO & WIPO 2007


(KO) 본 발명은 통상적으로 산업상 셀레늄을 보존하는데 사용되는 질산염 또는 아질산염은 배제하고 망간 화합물을 포함시킴으로써 셀레늄을 함유하는 유리에 셀레늄을 잔류시키는 방법이다. 특히, 바람직한 실시 양태는 착색제로서 셀레늄을 포함하는 회색 소다-석회-실리카 유리 조성물을 제조하는 것을 포함하며, 상기 회색 소다-석회-실리카 유리의 성분은 산화철, FeO0.9 내지 1.9 중량%, 산화 망간, MnO0.10 내지 1.0 중량%, 셀레늄, Se 0.0010 내지 0.0060 중량%, 산화 코발트, Co 0.002 내지 0.025 중량% 및 산화티탄, TiO0 내지 1.0 중량%를 필수 성분으로 하는 착색제를 가지며, 이들을 배합하고 용융하여 유리 조성물을 형성한다. 유리 조성물은 두께 4.0 ㎜에서 다음과 같은 분광 특성을 갖는다: 일루미넌트 A (Illuminant, LTA)를 사용하여 측정한 광투과율이 10 내지 55%이고, 자외선 (UV) 투과율이 25% 미만이고, 측정한 적외선 (IR) 투과율이 50% 미만임. 2 3 2 2