1. EP2451986 - NICKEL BASE SUPERALLOY

Office European Patent Office
Application Number 10726136
Application Date 01.07.2010
Publication Number 2451986
Publication Date 16.05.2012
Publication Kind B2
IPC
C22C 19/05
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
19Alloys based on nickel or cobalt
03based on nickel
05with chromium
CPC
C22C 19/057
CCHEMISTRY; METALLURGY
22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
CALLOYS
19Alloys based on nickel or cobalt
03based on nickel
05with chromium
051and Mo or W
057with the maximum Cr content being less 10%
Applicants ANSALDO ENERGIA SWITZERLAND AG
Inventors NAZMY MOHAMED
KÜNZLER ANDREAS
GERDES CLAUS PAUL
Designated States
Priority Data 10692009 09.07.2009 CH
2010059368 01.07.2010 EP
Title
(DE) NICKEL-BASIS-SUPERLEGIERUNG
(EN) NICKEL BASE SUPERALLOY
(FR) SUPERALLIAGE A BASE DE NICKEL
Abstract
(DE)
Die Erfindung betrifft eine Nickel-Basis-Superlegierung. Die erfindungsgemässe Legierung ist gekennzeichnet durch folgende chemische Zusammensetzung (Angaben in Gew.- %): 7.7-8.3 Cr, 5.0-5.25 Co, 2.0-2.1 Mo, 7.8-8.3 W, 5.8-6.1 Ta, 4.9-5.1 Al, 1.0-1.5 Ti, 1.0-2.0 Re, 0.11-0.15 Si, 0.1- 0.7 Hf, 0-0.5 Nb, 0.02-0.17 C, 50-400 ppm B, Rest Ni und herstellungsbedingte Verunreinigungen. Sie zeichnet sich durch eine sehr hohe Oxidationsbeständigkeit, Korrosionsbeständigkeit und gute Kriecheigenschaften bei hohen Temperaturen aus.

(EN)
The invention relates to a nickel-based superalloy. The alloy according to the invention is characterized by the following chemical composition (listed in % by weight): 7.7-8.3 Cr, 5.0-5.25 Co, 2.0-2.1 Mo, 7.8-8.3 W, 5.8-6.1 Ta, 4.9-5.1 Al, 1.0-1.5 Ti, 1.0-2.0 Re, 0.11-0.15 Si, 0.1- 0.7 Hf, 0-0.5 Nb, 0.02-0.17 C, 50-400 ppm B, remainder Ni and production-related impurities. It is characterized by very high oxidation resistance, corrosion resistance, and good creep properties at high temperatures.

(FR)
L'invention concerne un superalliage à base de nickel, caractérisé selon l'invention par la composition chimique suivante (données en pourcentage de poids): 7.7-8.3 Cr, 5.0-5.25 Co, 2.0-2.1 Mo, 7.8-8.3 W, 5.8-6.1 Ta, 4.9-5.1 Al, 1.0-1.5 Ti, 1.0-2.0 Re, 0.11-0.15 Si, 0.1- 0.7 Hf, 0-0.5 Nb, 0.02-0.17 C, 50-400 ppm B, pourcentage restant Ni et des impuretés inhérentes à la préparation. Ce superalliage se caractérise par une grande résistance à la corrosion et à l'oxydation et par une bonne résistance au fluage à des températures élevées.